wegottees · August 12th, 2008

alright i giving jpss a try i bought 100 11x17 sheets .. i was using new milford, i would like to hear answers from experienced users of the jpss, for lights..

i have a mighty press...15x15

questions are??

1. what is the press time for lights jpss

2. any other additional tips that you can tell me about jpss. because i dont want to waste...

3. whats up with this cracking situation, i cant AFFORD TO HAVE CUSTOMERS COMING BACK WANTING REFUNDS!!!!

MotoskinGraphix · August 12th, 2008

30 seconds heavy pressure
peel hot and slightly stretch tee
optional repress 5 seconds with a teflon sheet.

You will be good to go and the more pressure the better.

wegottees · August 12th, 2008

SOUNDS PRETTY EASY TO ME, SO IS JPSS YOUR MAIN LIGHT TRANSFER!!!

HOW HIGH IS THE TEMPERATURE WHEN U PRESS FOR 30 SECS

AND WHAT DOES THE REPRESS DO///

I HAVE A TEFLON SHEET, DO I PLACE IT OVER THE JPSS THE FIRST PRESS. I NORMALLY DONT USE THE PARCHMENT PAPER I USE MY TEFLON SHEET!!!

THANKS FOR YOUR REPLY

LIKE I SAID I CANT AFFORD TO FOR ANY THING TO GO WRONG, I WAS USING A NEW MILFORD, BUT I KEPT HEARING SUCH GREAT THINGS ABOUT JPSS, BUT THEN I HEAR BAD THINGS TOO, MAINLY THE CRACKING ISSUE, AND THEN BLEEDING??

BUT ANY TIPS WOULD BE GREAT

sorry i used caps

Danger Mouse · August 12th, 2008

I press 30 seconds at 375. Has been working well for me.

jumpman21 · August 12th, 2008

370 for 25-30 sec. very slight stretch ( when customer pulls on shirt, it will not look like it's cracked)......If possible, try both hot-peel & cold-peel and let us know what you think

thall17 · August 12th, 2008

375 20 seconds here

badalou · August 12th, 2008

Quote:

Originally Posted by wegottees


	SOUNDS PRETTY EASY TO ME, SO IS JPSS YOUR MAIN LIGHT TRANSFER!!! HOW HIGH IS THE TEMPERATURE WHEN U PRESS FOR 30 SECS AND WHAT DOES THE REPRESS DO/// I HAVE A TEFLON SHEET, DO I PLACE IT OVER THE JPSS THE FIRST PRESS. I NORMALLY DONT USE THE PARCHMENT PAPER I USE MY TEFLON SHEET!!! THANKS FOR YOUR REPLY LIKE I SAID I CANT AFFORD TO FOR ANY THING TO GO WRONG, I WAS USING A NEW MILFORD, BUT I KEPT HEARING SUCH GREAT THINGS ABOUT JPSS, BUT THEN I HEAR BAD THINGS TOO, MAINLY THE CRACKING ISSUE, AND THEN BLEEDING?? BUT ANY TIPS WOULD BE GREAT sorry i used caps

as one of the first people that used JPSS (In fact if you go to google and do a search for jet pro SofStretch I will come up second, how neat is that) I have never had bleeding. I have never had cracking. The people above have used it with same results. Lou

wegottees · August 12th, 2008

the question i have now is...when u quickly hot peel u still see a lil of the image on the transfer paper, is this normal?? because when i use ironall all the ink is removed from the transfer paper, and i cant see any of the image left on shhet

MotoskinGraphix · August 13th, 2008

I always have a ghost image left on the paper especially yellow using my epson c-120.

treadhead · August 13th, 2008

Yep....375 deg...30 secs...medium to heavy pressure. Stretch shirt after peeling transfer.

Not sure what the peeling issue is..just saw the post last night but I haven't had any issues.

But...it's worth keeping an eye on. IronAll for darks was a great paper until somebody discovered the fading issue surfacing with the bad batch of paper.

Girlzndollz · August 13th, 2008

Quote:

Originally Posted by wegottees


	the question i have now is...when u quickly hot peel u still see a lil of the image on the transfer paper, is this normal?? because when i use ironall all the ink is removed from the transfer paper, and i cant see any of the image left on shhet

I still have an image on the paper with Ironall and JPSS. We may use different printers and inks, tho.

Terrell, I'm not sure where you are at, between our pm's and your threads, I am a little lost as to your progress. Where are you at with everything? Are you okay at this point? Everything good?